Magnetic core – shell Nanoparticles Containing I 3-as a Novel Catalyst for the Facial Synthesis of Imidazole Derivatives in Solvent-free Conditions

A novel Fe3O4@SiO2@(CH2)3N+Me3I3magnetite nanoparticle was prepared and utilized in the synthetic conversion of aldehydes to imidazole derivatives in solvent-free conditions. These functionalized magnetic core–shell nanoparticles (MNPs) were characterized by Standard technique such as TEM, SEM, EDX, FT-IR, XRD, and VSM. The work up of reaction was very simple containing only a magnetic decantation. This novel catalyst could be separated easily and recycled several times without any significant decreasing of catalytic activity.


INTRODUCTION
In the past quar ter of the centur y, nanoparticle catalysts have attracted chemists attention because of their unique properties both in the reaction and workup.However, according their simple separation, in addition of their nano size advantages, their application have been developed more and more 1 .In the other hand, most catalysts such as nano particles have some drawbacks in usual separation methods, for instance, filtration or centrifugation.These general methods lead to loss of catalysts and products over the reaction and process steps.The magnetic nano particles can omit or improve many of these drawbacks 2 .According the advantages of using magnetic nano particles, some of them have been introduced in organic chemistry and catalyst fields [3][4][5][6][7][8][9][10][11][12][13][14][15] .
Imidazoles and their derivatives are a big class in organic chemistry.They have been introduced and utilized for many years because of their unique biological activity 1 .Imidazoles were usually produced by the reaction between a carbonyl group and 1,2-diamine in the presence of a special reagent or forced reaction condition 2. The using of numbers of reagents and catalysts indicating the importance of these compounds in organic synthesis.However, the majority of these reagents and catalysts suffer from some drawback such as low yields of the products, tedious work up, toxic reagents, high cost, long reaction time and..... Therefore, introducing a new safe and green reagents are desirable.
In continue with our research about nano catalyst 16 , we report herein the synthesis of novel magnetically triiodide catalyst and its application to the synthesis of imidazole derivatives.The synthetic steps are summarized in scheme 1.The preparation of first magnetite particles as a magnetic core was performed by reaction between ferrous and ferric chloride with NH 4 OH.An inert layer of SiO 2 was coated around previous core.The outer surface modification was made through the grafting of amino propylsilane, conversion of amine group to fourth ammonium group and finally, adding the triiodide anion to nano particle surface.Moreover, this magnetic catalyst was characterized by known appropriate technique such as SEM, TEM, EDX, XRD, FT-IR and VSM.Finally, the produced catalyst was used as a novel catalyst for the synthesis of imidazole derivatives.
Then the produced nano particles washed with water several times and dried in air.Afterward, this nano particle was dispersed in ethanol (20 ml) by ultrasonic treatment and a solution of I 2 in ethanol was added to dispersed solution and was stirred for one day.The resulting dark violet nano catalyst was collected by an external magnet and washed with 5 mL ethanol.

General procedure
A solution of substrate (1 mmol), aryl aldehyde (1 mmol), and Fe 3 O 4 @SiO 2 @(CH 2 ) 3 N+Me 3 I 3 -MNPs (0.007 gr) was heated at 100 °C under magnetic stirring for the requested reaction time.The complication of reaction was demonstrate by TLC.The EtOH (10 mL) was added and the reined nano particles was collected by an external magnet.The mixture was poured into ice-water (30 mL) and the pure heterocyclic product was filtered, washed with ice-water, and dried.

Characterization of magnetic nanoparticle TEM analysis
The size and morphology of the prepared novel catalyst were characterized by TEM (Fig. 1).
The TEM observation indicates all prepared nano particles have almost spherical core-shell structure (Fig. 1).The size of magnetic core is less than 20 nm and the diameter of all layers a shell are around 30 nm.

SEM analysis
The Scanning Microscope Electronic (SE) images indicate size and morphology of prepared nano particles (Fig. 2).According this data, all nano particles have a spherical shape with a large surface area.These images show that Fe 3 O 4 is spherically with nano dimensions less than 15 nm, but when TEOS coated The Fe 3 O 4 the average sizes increase to 20 nm (Fig. 2b).Furthermore, the SEM observation of Fe 3 O 4 @SiO 2 @APTES determined a recognizable layers on Fe 3 O 4 magnetic core (Fig. 2c).Finally, Fig. 2d shows the structure of Fe 3 O 4 @SiO 2 @(CH 2 ) 3 N+Me 3 I 3 -as core shell structure with average size of particles less than 50 nm.x-ray diffraction XRD pattern of pure magnetic nano catalyst are showed in Fig 3 .The most intense peak shows the average sizes of nano particles according Debye-Scherrer's formula D = 0.9λ/β cosθ, (D= the average crystalline size; λ= X-ray wavelength (1.542 Å); β= the angular line width of half-maximum intensity; θ= Bragg's angle in degree) 19,20 .Based on this data averages sizes of synthesized nano particles are less than 50 nm that confirm the SEM and TEM data.

EDS analysis
Duo to EDS patterns, clearly show the presence of N, C, O, Si, Fe and I (Fig. 4).The presence of Fe indicate iron oxide in nano articles.The higher intensity signals of Si and O, in addition, shows the grafting of SiO 2 layer to magnetic core.The signal of C proves the presence of this element in the structure of nano particle.Likewise, the N and I signal demonstrate the alkylated ammonium group and triiodide anion respectively.

FTIR spectrosocpy
In the Fig. 5a-cthe FT-IR spectra of all prepared nano particles are showed.The Fe-O bond showed a significant signal in 585 cm -1 21 .It is noticeable that Si-OH and Si-O-Si groups were confirmed by bands at 804, 951 and 1086 cm −1 .The stretching vibration of -OH group was confirmed by a broad band at 3300 -3500 cm −1 (Fig. 5b).The significant bands at 2965 and 2850 cm −1 belong to the stretching vibration of C-H bond of propyl amine group of APTES, which prove the successful grafting of this on silica layer.Furthermore, a band at 1440 cm −1 belong to the tertiary amine group.Overall, these results confirm that this novel nano particles successfully prepared.

Magnetic properties
The magnetization curve of Fe 3 O 4 , silica coated Fe 3 O 4 and Fe 3 O 4 @SiO 2 @(CH 2 ) 3 N+Me 3 I 3 -are presented in Fig. 6a-c.This kind of characterization would be called vibrating sample magnetometer (VSM).As can be seen from the diagrams, the magnetization of bare Fe 3 O 4 MNPs is about 60.0 emu/g at room temperature 23 .When the layers were added, the saturation magnetization would be decrease more and more.In fact, the saturation magnetization of Fe 3 O 4 @SiO 2 @(CH 2 ) 3 N+Me 3 I 3would be around 40 emu/g, which is lower than the bare one.Decrease of the saturation magnetization result from the creation of a silica shell around the Fe 3 O 4 core.

Optimization of nano catalyst for imidazole synthesis
The reaction process is simple and fast and proceeded in excellent yields of products.At the first step, the conversion reaction carried out in different protic and aprotic solvents and the product yields compared to solvent free condition (Table 1).The imidazoles preparation reaction was performed in the both solvent and solvent free conditions.As regard the first, a verity of different solvents were utilized for this conversion, such as diethyl ether, ethanol, dichloromethane, THF, toluene, acetonitrile, and DMF.Although, very low yield of products were obtained in the presence of DMF as solvent, but no one performed a noticeable yields.As can be seen from the Table 1 only solvent free condition is the best case for this reaction.Likewise, the catalyst amount's effect was explored on reaction time and yields Table 2).Although, in the absence of this catalyst no products were found, but there are two basic trends in the presence of different amount of catalyst.The yield of products went up by increasing the catalyst amount from 0.025 to 0.07 g.But with higher amount of catalyst the yield of products were leveled off.
In general, all data show significantly that the best reaction condition is the solvent free at 100 °C in the presence of 0.07g of periodate magnetic nano catalyst.
The results of condition's optimization were used in the reaction of a variety of aldehyde derivatives with 1,2-diamino benzene to synthesis of some heterocyclic compounds (Table 3).

Synthesis of imidazole, thiazole and pirimidine derivatives using Fe 3 O 4 @SiO 2 (CH 2 ) 3 N+Me 3 I 3 -
As can be seen from the Table 3, there are 15 examples for catalytic conversion of aldehyde to the corresponding heterocyclic compounds using this novel catalyst containing I 3 -.The yields are excellent and the procedure is very simple.Likewise, the work up is easy too.The catalyst is readily separated by only using an external magnet.

Catalyst recovery and its stability
The reaction of 4-chlorobenzaldehyde and o-phenylene diamine in the presence of the catalytic amount of Fe 3 O 4 @SiO 2 @(CH 2 ) 3 N+Me 3 I 3was performed for demonstrate recoverability of this catalyst.The catalyst was recycle and reused for five times without any losing of its activity.In fact, this unique nano catalyst could be recycled and reused times and times (Fig. 7).On the other hands, the catalyst shows very good shelf life too.This novel catalyst last for months.So, it can be stored for months without significant decline in its activity.

CONCLUSION
In this manuscript, we herein report a novel magnetic nano catalyst containing periodide (Fe 3 O 4 @SiO 2 @(CH 2 ) 3 N+Me 3 I 3 -) as a green, efficient and recoverable nano catalyst.The separation of this catalyst from reaction mixture is very simple too.It could be isolated using an external magnet vessel.The imidazole, thiazole, and pirimidine derivatives could be easily prepared using this novel nano catalyst in excellent yields.

Table 1 : Effect of different solvent on product yield for the synthesis of 2-(4-chlorophenyl)- 1H-benzimidazole
(1mmol), and nano catalyst (0.07 g).a) reflux condition, b) in solvent-free condition at 50 o C, c) in solvent-free condition at 75 o C, d) in solvent-free condition at 100 o C